Plunger Lubricant Granule

Outline:
Punch lubricant particles, it does not contain sub-containing graphite and graphite. Product particle size is divided into: Φ 1.0~1.5mm, Φ 1.5~2.0mm, Φ 2.0~3.0mm, the injection sleeve and it Plunger top melting and rapid expansion through its excellent capillary effect in the injection sleeve to form a lubricating film with excellent performance. It is easy to use without a traditional oil-based or water-based products used in dispensing pump-spray system.

Advantage:
1, no general pollution generated by oil lubricant;
2, reduce the incidence of casting porosity;
3, to extend the plunger tube life, reduce adverse effects due to friction;
4, with a punch to the die casting plant life, usually with pure oil lubrication than tripled;
5, increase injection speed;
6, casting particles completely consumed, no oil pollution;
7, no oil marks casting surface, the surface clean and bright;
8, pouring mouth, flow, soup cake recycling used, no grease, smoke, air pollution;
9, do not waste water, without water cooling system and cleaning the injection head;
10, the amount of a province, can achieve cost savings;
11, to improve process safety;
12, to maintain plant, ceilings, floors clean, green environmental protection in line with modern requirements.

White particles:
Structure/shape: Without graphite, beaded ball
20ºC, density: 0.5-0.7cm3
Color: White
Melting point: 120-130ºC
Scope: 50-120mm in diameter between the injection sleeve

Black particles:
Structure/shape: Without graphite, beaded ball
20ºC, density: 0.5-0.7 cm3
Color: White
Melting point: 131ºC
Scope: 50-160mm in diameter between the injection sleeve.

Instructions for use:
Transmitter will be joined by particle particles pouring Room
Use of the punch diameter for different
60mm0.4-0.5g
80mm0.6-0.8g
100mm1.0-1.3G
140mm1.7-2.5g
>150mm2.2-4.0g
Used to determine the amount depends on the casting weight to be triedby the experience.

25kg/woven bag 25kg/drum